从松节油中高效分离α-蒎烯

设计出一种从松节油中高效分离α-蒎烯的蒸馏-分馏工艺，对工艺条件进行了优化研究，产物经气相色谱-质谱联用测定、红外光谱结构表征，确证为α-蒎烯，纯度为98．76％，收率达到72．92％。     

Preparation of fluoroacrylate nanocopolymer by miniemulsion polymerization used in textile finishing

Latex based on fluoroacrylate (TAN) and other comonomers was prepared via miniemulsion polymerization in the presence of stearyl trimethyl ammonium chloride (STAC) and 2, 2′‐azobis (2‐amidinopropane) dihydrochloride (ABAP) as a water soluble initiator. Light transmittance studies demonstrated that the light transmittance of prepared emulsions increases with the amount of TAN, STAC, cosolvent DPM, and hydrophobe DM. Given suitable reaction temperature and quantities of TAN, STAC, DPM, and DM, a copolymer emulsion of fluoroacylate with a particle size of 50 nm was produced. The water repellency tested on polyester fabrics displayed greater effectiveness than that of commercial products with higher fluorine content. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 94: 1466–1472, 2004     

聚乳酸的熔融聚合法的改进研究

采用熔融聚合法合成聚乳酸,对实验条件进行了优化选择。筛选出SnC l2为最适宜催化剂进行熔融聚合。最佳工艺条件为:催化剂用量为0.5%质量分数,反应温度为180℃,反应时间7.5 h,同时利用搅拌与鼓泡真空法使缩聚后期体系粘稠大搅拌脱水困难问题进一步得到解决,使熔融聚合产物的粘均分子量Mη达83483。     

超临界流体中的酶催化反应及研究进展

叙述了介质水含量、温度、压力、底物、产物含量及夹带剂等因素对超临界流体中酶催化反应的影响,并对超临界流体对手性药物的拆分和合成方法进行了归纳和综合。超临界流体中的酶催化已经有了一定研究,但目前大部分研究工作只停留在实验研究,而且流体和酶的选择过于集中。因此,如何使得这项技术应用于实际的大生产,尤其是在手性药物合成和拆分方面的应用将是今后研究的方向。     

改善操作延长转化炉炉管寿命

分析转化炉炉管不正常原因及对炉管造成的危害，确定通过改善工艺操作来延长转化炉炉管寿命，实践证明效果明显。     

利用3ω法同时测量纳米流体热导率和热扩散系数

提出了应用基于谐波探测技术的3ω法进行液体导热性能测量的方法。设计了3ω测试系统，测试了不同浓度和不同温度下纳米流体的热导率和热扩散系数，与文献中的测试结果进行了对比。实验中测试的热波信号较好地满足频域内的导热方程，说明采用交流电流加热可使流体的微对流作用得到有效减弱。采用基于多颗粒布朗运动的微对流（MSBW）模型预测了纳米流体的热导率。浓度比较低时TiO₂+蒸馏水、Al₂ O₃+蒸馏水纳米颗粒流体的热导率随温度增加呈线性增大，并且与液体的Prandtl数有关，在测试温度为18～65℃范围内，水的热导率随温度升高以及纳米颗粒的布朗运动所引起周围基液的微对流作用是纳米流体强化传热的两个重要机理。     

Al2O3-Al-C材料加热过程的变化

按w(板状刚玉)=84%,w(铝粉)=8%,w(α-Al2O3微粉)=6%,w(鳞片石墨)=2%的配比配料,外加3%热固性酚醛树脂作结合剂,成型后于200℃烘烤24h。在埋炭条件下于600～1400℃保温3h加热处理,冷却后测量试样的线变化率、显气孔率和常温耐压强度,并分析部分试样的孔径分布、相组成和显微结构,同时测定烘烤后试样在600℃、800℃、1000℃、1200℃和1400℃下的热态抗折强度,以分析该材料在加热过程的变化。结果表明,试样在600～1400℃埋炭加热过程中的变化可大致分为3个阶段:1)600～800℃,金属Al于660℃熔化,促进试样致密化,在800℃时已有少量Al4C3和AlN生成,使加热后试样的致密度和强度增大;2)800～1200℃,大量生成Al4C3和AlN,Al4C3和AlN填充在刚玉骨架结构中,试样的显气孔率进一步减小,常温耐压强度和热态抗折强度进一步增大;3)1200～1400℃,金属Al消失,Al4C3含量减少,部分与N2反应转化为AlN,试样的显气孔率略有降低,常温耐压强度和热态抗折强度略有增大。由此可见,随着加热温度的提高,材料的结合方式从碳结合转变为碳和金属铝复合结合,最后逐渐转变为碳和非氧化物复合结合。     

火焰原子吸收光谱法测定百合中的微量元素

本文利用火焰原子吸收光谱法测定了百合中的钙、镁、铁、锰、锌、铜、钴、钾等金属元素含量。百合经过硝酸、高氯酸处理后，再用原子吸收分光光度法测定其微量元素含量。此法快速、简单，结果准确。     

Synthesis and optical properties of polyacetylenes containing nonlinear optical chromophores

High molecular weight polyacetylenes bearing nonlinear chromophoric pendants poly[4-ethynyl-4′-(N,N-diethylamino)azobenzene-co-phenylacetylene]s [poly(EAAB-co-PA)s] were synthesized in moderate yields by [Rh(nbd)Cl]₂-Et₃N. The azo unit in the copolymers can be effectively controlled by the monomer feed ratio. Whereas the homopolymer of EAAB possessed low solubility, all the copolymers, however, dissolved readily in common organic solvents when the poly(EAAB) molar content was less than 41.7%. The structures and properties of the polymers were characterized and evaluated by UV, NMR, optical limiting, and nonlinear optical analyses. All the copolymers possessed high stereoregularity and thermal stability (≥300 °C). They can attenuate intense laser pulses, with solutions of high concentrations showing better performances. The third-order nonlinear susceptibility of the copolymers was as high as 4.62×10⁻¹¹ esu, which are two orders of magnitude larger than those of poly(PA), and larger than that of poly(N-carbazoylacetylene), and poly(1-naphthylacetylene).     

异氰酸酯改性光敏水性环氧丙烯酸酯的合成

以双酚A型环氧树脂与丙烯酸反应合成了具有羟基侧基的环氧丙烯酸酯，再用甲苯二异氰酸酯与内烯酸-β-羟乙酯的半加成物对上述环氧丙烯酸酯树脂进行接枝改性，再用酸酐引入羧基，经胺中和后，水性化．可得较为稳定的自乳化光敏树脂水分散体系。通过化学测试和IR解析．确定了合成条件、合成终点及产物结构，并以此为基料配成紫外光固化涂料，所得涂层性能优异。